Metals -> Bronze -> Tin foundry bronzes Characteristics of the material BrO8TS4 ( BrO8TS4, ÁðÎ8Ö4 ).
Material : BrO8TS4 ( BrO8TS4, ÁðÎ8Ö4 ) Classification : Tin foundry bronzes
Chemical composition in % of the material BrO8TS4 ( BrO8TS4, ÁðÎ8Ö4 ) . Fe Si P Al Cu Pb Zn Sb Sn Impurity max 0.3 max 0.02 max 0.05 max 0.02 84 - 89 max 0.5 4 - 6 max 0.3 7 - 9 all 1
Comment: Cu is a basis; the percentage of Cu is given approximately. Mechanical properties under Ò=20o Ñ of the material BrO8TS4 ( BrO8TS4, ÁðÎ8Ö4 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - cast in a metal mould 196 10 Without heat treatment sand (mould) casting 196 10 Without heat treatment
Brinell hardness of the material BrO8TS4 ( BrO8TS4, ÁðÎ8Ö4 ) (without heat treatment) , HB 10 -1 = 75 MPa
Physical properties of the material BrO8TS4 ( BrO8TS4, ÁðÎ8Ö4 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.98 16.6 68.2 8800 356 135
Friction coefficient of the material BrO8TS4 ( BrO8TS4, ÁðÎ8Ö4 ) . Friction coefficient with oil
: 0.006 Friction coefficient without oil
: 0.3
Technological properties of the material BrO8TS4 ( BrO8TS4, ÁðÎ8Ö4 ) . Melting temperature, °C : 1000 Casting temperature, °C : 1100 - 1150 Linear shrinkage, % : 1.47
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû