Metals -> Copper-zinc alloy (latten, brass) -> Copper-zinc alloys pressure treated Characteristics of the material L80 ( L80, Л80 ).
Material : L80 ( L80, Л80 ) Classification : Copper-zinc alloys pressure treated
Chemical composition in % of the material L80 ( L80, Л80 ) . Fe P Cu Pb Zn Sb Bi Impurity max 0.1 max 0.01 79 - 81 max 0.03 18.7 - 21 max 0.005 max 0.002 all 0.3
Comment: Zn is a basis; the percentage of Zn is given approximately. Mechanical properties under Т=20o С of the material L80 ( L80, Л80 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - hard 610-680 2-5 soft 300-350 45-55
Brinell hardness of the material L80 ( L80, Л80 ) , hard HB 10 -1 = 140 - 150 MPa Brinell hardness of the material L80 ( L80, Л80 ) , soft HB 10 -1 = 55 - 65 MPa
Physical properties of the material L80 ( L80, Л80 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.1 142 8660 60 100 18.8 399.4
Friction coefficient of the material L80 ( L80, Л80 ) . Friction coefficient with oil
: 0.015 Friction coefficient without oil
: 0.71
Technological properties of the material L80 ( L80, Л80 ) . Melting temperature, °C : 1000 Forging temperature,°C : 700 - 850 Annealing temperature, °C : 500 - 650
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены