Metals -> Copper-zinc alloy (latten, brass) -> Copper-zinc alloys pressure treated Characteristics of the material LO62-1 ( LO62-1, ЛО62-1 ).
Material : LO62-1 ( LO62-1, ЛО62-1 ) Classification : Copper-zinc alloys pressure treated
Chemical composition in % of the material LO62-1 ( LO62-1, ЛО62-1 ) . Fe P Cu Pb Zn Sb Bi Sn Impurity max 0.1 max 0.01 61 - 63 max 0.1 35.6 - 38.3 max 0.005 max 0.002 0.7 - 1.1 all 0.3
Comment: Zn is a basis; the percentage of Zn is given approximately. Mechanical properties under Т=20o С of the material LO62-1 ( LO62-1, ЛО62-1 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - hard 680-750 5-10 soft 380-430 38-44
Brinell hardness of the material LO62-1 ( LO62-1, ЛО62-1 ) , hard HB 10 -1 = 140 - 150 MPa Brinell hardness of the material LO62-1 ( LO62-1, ЛО62-1 ) , soft HB 10 -1 = 75 - 85 MPa
Physical properties of the material LO62-1 ( LO62-1, ЛО62-1 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.05 108.9 8500 78 100 19.3
Technological properties of the material LO62-1 ( LO62-1, ЛО62-1 ) . Melting temperature, °C : 906 Forging temperature,°C : 700 - 780 Annealing temperature, °C : 550 - 650
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены