Metals -> Copper-zinc alloy (latten, brass) -> Copper-zinc alloys pressure treated Characteristics of the material LS64-2 ( LS64-2, ËÑ64-2 ).
Material : LS64-2 ( LS64-2, ËÑ64-2 ) Classification : Copper-zinc alloys pressure treated
Chemical composition in % of the material LS64-2 ( LS64-2, ËÑ64-2 ) . Fe P Cu Pb Zn Sb Bi Impurity max 0.1 max 0.01 63 - 66 1.5 - 2 31.7 - 35.5 max 0.005 max 0.002 all 0.3
Comment: Zn is a basis; the percentage of Zn is given approximately. Mechanical properties under Ò=20o Ñ of the material LS64-2 ( LS64-2, ËÑ64-2 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - hard 580-670 4-6 soft 320-380 55-65
Brinell hardness of the material LS64-2 ( LS64-2, ËÑ64-2 ) , hard HB 10 -1 = 140 - 150 MPa Brinell hardness of the material LS64-2 ( LS64-2, ËÑ64-2 ) , soft HB 10 -1 = 50 - 60 MPa
Physical properties of the material LS64-2 ( LS64-2, ËÑ64-2 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.05 117 8500 70 100 20.3
Friction coefficient of the material LS64-2 ( LS64-2, ËÑ64-2 ) . Friction coefficient with oil
: 0.1 Friction coefficient without oil
: 0.22
Technological properties of the material LS64-2 ( LS64-2, ËÑ64-2 ) . Melting temperature, °C : 910 Annealing temperature, °C : 620 - 670
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû