Metals -> Copper-zinc alloy (latten, brass) -> Copper-zinc alloys pressure treated

Characteristics of the material LZHS58-1-1   ( LZHS58-1-1,   58-1-1 ).

Material : LZHS58-1-1   ( LZHS58-1-1,   58-1-1 )
Classification : Copper-zinc alloys pressure treated


Chemical composition in % of the material LZHS58-1-1   ( LZHS58-1-1,   58-1-1 ) .
Fe P Cu PbZn Sb Bi Impurity
0.7 - 1.3max   0.0256 - 580.7 - 1.338.9 - 42.6max   0.01max   0.003 all 0.5
Comment: Zn is a basis; the percentage of Zn is given approximately.


Mechanical properties under =20o of the material LZHS58-1-1   ( LZHS58-1-1,   58-1-1 ) .
Assortment Dimension Direct. s sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
hard     650-750  2-5   
soft     350-450  35-45   


    Brinell hardness of the material   LZHS58-1-1   ( LZHS58-1-1,   58-1-1 )   ,     hard HB 10 -1= 160 - 170   MPa
    Brinell hardness of the material   LZHS58-1-1   ( LZHS58-1-1,   58-1-1 )   ,     soft HB 10 -1= 75 - 85   MPa


Physical properties of the material LZHS58-1-1   ( LZHS58-1-1,   58-1-1 ) .
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(mGrade) kg/m3 J/(kgGrade) Ohmm
20 1.06   108.9 8400   70
100   20.4        


Technological properties of the material LZHS58-1-1   ( LZHS58-1-1,   58-1-1 ) .
 Melting temperature, C : 895
 Annealing temperature, C : 600 - 650



Specification :
Mechanical properties :
s - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(mGrade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kgGrade)]
R - Electrical resistance , [Ohmm]

Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others).
Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal trader

Top

©   2003 - 2009   All rights reserved.       About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user



| | | |
© 2002 - 2009 .
 
-12345-