Metals -> Copper -> Copper-nickel alloys Characteristics of the material MN16 ( MN16, МН16 ).
Material : MN16 ( MN16, МН16 ) Classification : Copper-nickel alloys
Chemical composition in % of the material MN16 ( MN16, МН16 ) . Ni+Co Fe C Si S P Cu As Pb Mg Sb Bi Impurity 15.3 - 16.3 max 0.05 max 0.03 max 0.002 max 0.002 max 0.002 83.5 - 84.7 max 0.002 max 0.002 max 0.05 max 0.002 max 0.002 all 0.2
Comment: Cu is a basis; the percentage of Cu is given approximately. Mechanical properties under Т=20o С of the material MN16 ( MN16, МН16 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - soft 300-380 25-35 hard 500-600 4-6
Brinell hardness of the material MN16 ( MN16, МН16 ) , soft HB 10 -1 = 70 MPa Brinell hardness of the material MN16 ( MN16, МН16 ) , hard HB 10 -1 = 122 MPa
Physical properties of the material MN16 ( MN16, МН16 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.8 9020 223 100 15.3
Technological properties of the material MN16 ( MN16, МН16 ) . Melting temperature, °C : 1170 Forging temperature,°C : 950 - 1030 Annealing temperature, °C : 700 - 780
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены