Metals -> Copper -> Copper-nickel alloys Characteristics of the material MNTSS16-29-1.8 ( MNTSS16-29-1.8, ÌÍÖÑ16-29-1.8 ).
Material : MNTSS16-29-1.8 ( MNTSS16-29-1.8, ÌÍÖÑ16-29-1.8 ) Classification : Copper-nickel alloys
Chemical composition in % of the material MNTSS16-29-1.8 ( MNTSS16-29-1.8, ÌÍÖÑ16-29-1.8 ) . Ni+Co Cu Pb Zn Impurity 15 - 16.5 51 - 55 1.6 - 2 27.5 - 34 all 1
Comment: Zn is a basis; the percentage of Zn is given approximately. Mechanical properties under Ò=20o Ñ of the material MNTSS16-29-1.8 ( MNTSS16-29-1.8, ÌÍÖÑ16-29-1.8 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - soft 350-450 40-45 hard 600-700 2-4
Physical properties of the material MNTSS16-29-1.8 ( MNTSS16-29-1.8, ÌÍÖÑ16-29-1.8 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.27 8800
Technological properties of the material MNTSS16-29-1.8 ( MNTSS16-29-1.8, ÌÍÖÑ16-29-1.8 ) . Melting temperature, °C : 1120 Annealing temperature, °C : 700 - 750
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû