Metals -> Zinc -> Primary zinc Characteristics of the material TSV0 ( ЦВ0 ).
Material : TSV0 ( ЦВ0 ) Classification : Primary zinc
Chemical composition in % of the material TSV0 ( ЦВ0 ) . Fe Cu Pb Zn Sn Cd Impurity max 0.002 max 0.001 max 0.003 min 99.995 max 0.001 max 0.002 all 0.005
Mechanical properties under Т=20o С of the material TSV0 ( ЦВ0 ) .
Assortment Dimension Direct. s в s T
d 5
y KCU Heat treatment - mm - MPa MPa % % kJ / m2 - casted 120-140
Brinell hardness of the material TSV0 ( ЦВ0 ) , casted HB 10 -1 = 30 - 40 MPa Brinell hardness of the material TSV0 ( ЦВ0 ) , deformed HB 10 -1 = 35 - 45 MPa
Physical properties of the material TSV0 ( ЦВ0 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.95 7130 100 39.5
Technological properties of the material TSV0 ( ЦВ0 ) . Forging temperature,°C : 150 - 170 Casting temperature, °C : 430 - 450 Linear shrinkage, % : 1.57
Specification :
Mechanical properties : s в - Tensile strength , [MPa] s T - Yield stress, [MPa] d 5 - Specific elongation at fracture , [ % ] y - Reduction of area , [ % ] KCU - Impact strength , [ kJ / m2 ] HB - Brinell hardness , [MPa]
Physical properties : T - Test temperature , [Grade] E - Young modulus , [MPa] a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade] l - Termal (heat) condition coefficient , [Watt/(m·Grade)] r - Density , [kg/m3 ] C - Specific heat
( range 20o - T ), [J/(kg·Grade)] R - Electrical resistance , [Ohm·m]