Metals -> Zinc -> Primary zinc Characteristics of the material TS0А ( Ц0А ).
Material : TS0А ( Ц0А ) Classification : Primary zinc
Chemical composition in % of the material TS0А ( Ц0А ) . Fe Cu As Pb Zn Sn Cd Impurity max 0.003 max 0.001 max 0.0005 max 0.01 min 99.98 max 0.001 max 0.003 all 0.02
Mechanical properties under Т=20o С of the material TS0А ( Ц0А ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - casted 120-140 0.3-0.5 30 deformed 120-170 40-50 60-80
Brinell hardness of the material TS0А ( Ц0А ) , casted HB 10 -1 = 30 - 40 MPa Brinell hardness of the material TS0А ( Ц0А ) , deformed HB 10 -1 = 35 - 45 MPa
Physical properties of the material TS0А ( Ц0А ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.95 7130 100 39.5
Technological properties of the material TS0А ( Ц0А ) . Melting temperature, °C : 419.5 Forging temperature,°C : 150 - 170 Casting temperature, °C : 430 - 450 Linear shrinkage, % : 1.57
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены