Metals -> Aluminium alloy -> Technical aluminium Characteristics of the material ÀD0 ( ÀÄ0 ).
Material : ÀD0 ( ÀÄ0 ) Classification : Technical aluminium
Chemical composition in % of the material ÀD0 ( ÀÄ0 ) . Fe Si Mn Ti Al Cu Mg Zn Impurity max 0.3 max 0.3 max 0.025 max 0.1 min 99.5 max 0.02 max 0.03 max 0.07 other, each 0.03; all 0.5
Mechanical properties under Ò=20o Ñ of the material ÀD0 ( ÀÄ0 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Sheet annealed 80 40 35 80 Bar 150-100 40 6 60
Brinell hardness of the material ÀD0 ( ÀÄ0 ) , casted HB 10 -1 = 20 MPa Brinell hardness of the material ÀD0 ( ÀÄ0 ) , annealed HB 10 -1 = 25 MPa Brinell hardness of the material ÀD0 ( ÀÄ0 ) , deformed HB 10 -1 = 30 - 35 MPa
Physical properties of the material ÀD0 ( ÀÄ0 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.71 2710 29.2 100 24 226 200 25.6 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material ÀD0 ( ÀÄ0 ) . Melting temperature, °C : 658.7
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû