Metals -> Magnesium -> Primary magnesium Characteristics of the material Mg96 ( Мг96 ).
Material : Mg96 ( Мг96 ) Classification : Primary magnesium
Chemical composition in % of the material Mg96 ( Мг96 ) . Fe Si Mn Ni Al Cu Mg Na Impurity max 0.004 max 0.004 max 0.004 max 0.002 max 0.006 max 0.002 min 99.96 max 0.01 all 0.04
Mechanical properties under Т=20o С of the material Mg96 ( Мг96 ) .
Assortment Dimension Direct. s в s T
d 5
y KCU Heat treatment - mm - MPa MPa % % kJ / m2 - casted 85-130 3-6 deformed 250 8-10 annealed 180 15-17
Brinell hardness of the material Mg96 ( Мг96 ) , casted HB 10 -1 = 30 MPa Brinell hardness of the material Mg96 ( Мг96 ) , deformed HB 10 -1 = 50 MPa Brinell hardness of the material Mg96 ( Мг96 ) , annealed HB 10 -1 = 40 MPa
Physical properties of the material Mg96 ( Мг96 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.45 1740 47 100 26
Technological properties of the material Mg96 ( Мг96 ) . Melting temperature, °C : 651
Specification :
Mechanical properties : s в - Tensile strength , [MPa] s T - Yield stress, [MPa] d 5 - Specific elongation at fracture , [ % ] y - Reduction of area , [ % ] KCU - Impact strength , [ kJ / m2 ] HB - Brinell hardness , [MPa]
Physical properties : T - Test temperature , [Grade] E - Young modulus , [MPa] a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade] l - Termal (heat) condition coefficient , [Watt/(m·Grade)] r - Density , [kg/m3 ] C - Specific heat
( range 20o - T ), [J/(kg·Grade)] R - Electrical resistance , [Ohm·m]