Metals -> Lead -> Lead babbits Characteristics of the material B16 ( B16, Б16 ).
Material : B16 ( B16, Б16 ) Classification : Lead babbits
Chemical composition in % of the material B16 ( B16, Б16 ) . Fe Al Cu As Pb Zn Sb Bi Sn max 0.1 max 0.01 1.5 - 2 max 0.3 63.34 - 68.5 max 0.15 15 - 17 max 0.1 15 - 17
Comment: Pb is a basis; the percentage of Pb is given approximately. Mechanical properties under Т=20o С of the material B16 ( B16, Б16 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - 147 86
Brinell hardness of the material B16 ( B16, Б16 ) , HB 10 -1 = 30 MPa
Physical properties of the material B16 ( B16, Б16 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 9290
Technological properties of the material B16 ( B16, Б16 ) . Melting temperature, °C : 410
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены