Metals -> Magnesium -> Magnesium for casting Characteristics of the material ML2 ( МЛ2 ).
Material : ML2 ( МЛ2 ) Classification : Magnesium for casting
Chemical composition in % of the material ML2 ( МЛ2 ) . Fe Si Mn Ni Al Cu Ca Be Mg Zn Impurity max 0.08 max 0.1 1 - 2 max 0.01 max 0.1 max 0.1 max 0.1 max 0.002 97.5 - 99 max 0.05 all 0.5
Comment: Mg is a basis; the percentage of Mg is given approximately. Mechanical properties under Т=20o С of the material ML2 ( МЛ2 ) .
Assortment Dimension Direct. s в s T
d 5
y KCU Heat treatment - mm - MPa MPa % % kJ / m2 - 90 3 Without heat treatment 100 30 4 6 Without heat treatment
Brinell hardness of the material ML2 ( МЛ2 ) (without heat treatment) , HB 10 -1 = 35 MPa
Physical properties of the material ML2 ( МЛ2 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.43 133.9 1800 1046.7 100 27.3
Technological properties of the material ML2 ( МЛ2 ) . Solidification temperature, °C : 650 - 645 Casting temperature, °C : 750 - 800 Linear shrinkage, % : 1.6 - 1.9
Specification :
Mechanical properties : s в - Tensile strength , [MPa] s T - Yield stress, [MPa] d 5 - Specific elongation at fracture , [ % ] y - Reduction of area , [ % ] KCU - Impact strength , [ kJ / m2 ] HB - Brinell hardness , [MPa]
Physical properties : T - Test temperature , [Grade] E - Young modulus , [MPa] a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade] l - Termal (heat) condition coefficient , [Watt/(m·Grade)] r - Density , [kg/m3 ] C - Specific heat
( range 20o - T ), [J/(kg·Grade)] R - Electrical resistance , [Ohm·m]