Metals -> Copper -> High-temperature cooper alloy Characteristics of the material MKB ( MKB, МКБ ).
Material : MKB ( MKB, МКБ ) Classification : High-temperature cooper alloy
Comment: Cu is a basis; the percentage of Cu is given approximately. Mechanical properties under Т=20o С of the material MKB ( MKB, МКБ ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - 764 745 22 294
Brinell hardness of the material MKB ( MKB, МКБ ) , HB 10 -1 = 180 MPa Brinell hardness of the material MKB ( MKB, МКБ ) , deformed HB 10 -1 = 140 MPa Brinell hardness of the material MKB ( MKB, МКБ ) , annealed HB 10 -1 = 80 MPa
Physical properties of the material MKB ( MKB, МКБ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 197 8780 34.6
Technological properties of the material MKB ( MKB, МКБ ) . Forging temperature,°C : 750 - 950 Annealing temperature, °C : 700
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены