Metals -> Aluminium alloy -> Aluminium wrought alloys Characteristics of the material АK4-1 ( АК4-1 ).
Material : АK4-1 ( АК4-1 ) Classification : Aluminium wrought alloys
Chemical composition in % of the material АK4-1 ( АК4-1 ) . Fe Si Mn Ni Ti Al Cu Mg Zn Impurity 0.8 - 1.3 max 0.35 max 0.2 0.8 - 1.3 0.02 - 0.1 92.05 - 96.08 1.9 - 2.5 1.4 - 1.8 max 0.3 other, each 0.05; all 0.1
Comment: Al is a basis; the percentage of Al is given approximately. Mechanical properties under Т=20o С of the material АK4-1 ( АК4-1 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Sheet 380 310 6 200 Profile 400 330 8
Brinell hardness of the material АK4-1 ( АК4-1 ) , HB 10 -1 = 109 - 117 MPa
Physical properties of the material АK4-1 ( АК4-1 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.72 2800 55 100 20.8 146 797
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены