Characteristics of the material TSM10-2   ( TSM10-2,   10-2 ).

Material : TSM10-2   ( TSM10-2,   10-2 )
Classification : Zinc wrought alloys


Chemical composition in % of the material TSM10-2   ( TSM10-2,   10-2 ) .
Al Cu Mg Zn
10 - 102 - 20.03 - 0.0387.97 - 87.97
Comment: Zn is a basis; the percentage of Zn is given approximately.


Mechanical properties under =20o of the material TSM10-2   ( TSM10-2,   10-2 ) .
Assortment Dimension Direct. s sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
      350-450  15-2045-60  


    Brinell hardness of the material   TSM10-2   ( TSM10-2,   10-2 )   ,       HB 10 -1= 95 - 100   MPa


Physical properties of the material TSM10-2   ( TSM10-2,   10-2 ) .
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(mGrade) kg/m3 J/(kgGrade) Ohmm
20       6210    



Specification :
Mechanical properties :
s - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(mGrade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kgGrade)]
R - Electrical resistance , [Ohmm]

Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others).
Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal trader

Top

©   2003 - 2009   All rights reserved.       About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user



| | | |
© 2002 - 2009 .
 
-12345-