Metals -> High-temperature or heat-resistant steel and alloy -> High alloy high-temperature steel Characteristics of the material 15KH12VNMF ( 15H12VNMF, 15Õ12ÂÍÌÔ ).
Material : 15KH12VNMF ( 15H12VNMF, 15Õ12ÂÍÌÔ ) Classification : High alloy high-temperature steel
Chemical composition in % of the material 15KH12VNMF ( 15H12VNMF, 15Õ12ÂÍÌÔ ) . C Si Mn Ni S P Cr Mo W V Ti Cu 0.12 - 0.18 max 0.4 0.5 - 0.9 0.4 - 0.8 max 0.025 max 0.03 11 - 13 0.5 - 0.7 0.7 - 1.1 0.15 - 0.3 max 0.2 max 0.3
Temperature of critical points of the grade 15KH12VNMF ( 15H12VNMF, 15Õ12ÂÍÌÔ ).
Ac1 = 800 - 810 , Ac3 (Acm ) = 860 - 880
Mechanical properties under Ò=20o Ñ of the material 15KH12VNMF ( 15H12VNMF, 15Õ12ÂÍÌÔ ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Bar longitudinal 690 510 18 57 700 Guenching 1050o C, oil, Drawing 740o C,Cooling air, Bars 60 740 590 15 45 590 Annealing 900 - 950o C, oven, Guenching 1000 - 1020o C, oil, Drawing 600 - 700o C, air,
Brinell hardness of the material 15KH12VNMF ( 15H12VNMF, 15Õ12ÂÍÌÔ ) (annealing) , HB 10 -1 = 229 MPa
Physical properties of the material 15KH12VNMF ( 15H12VNMF, 15Õ12ÂÍÌÔ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.16 7850 100 10 24 477 200 10.5 25.5 498 300 2 10.7 25.9 545 400 1.94 11 26.3 625 500 1.84 11.2 26.8 741 600 1.66 11.6 27.2 896 700 27.2 800 27.6 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 15KH12VNMF ( 15H12VNMF, 15Õ12ÂÍÌÔ ) . Weldability: hard weldability.
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû