Metals -> Structural steel -> Spring structural steel Characteristics of the material 65G ( 65G, 65Г ).
Material : 65G ( 65G, 65Г ) Substitute: 70, У8А, 70Г, 60С2А, 9ХС, 50ХФА, 60С2, 55С2 Classification : Spring structural steel
Chemical composition in % of the material 65G ( 65G, 65Г ) . C Si Mn Ni S P Cr Cu 0.62 - 0.7 0.17 - 0.37 0.9 - 1.2 max 0.25 max 0.035 max 0.035 max 0.25 max 0.2
Temperature of critical points of the grade 65G ( 65G, 65Г ).
Ac1 = 721 , Ac3 (Acm ) = 745 , Ar3 (Arcm ) = 720 , Ar1 = 670 , Mn = 270
Mechanical properties under Т=20o С of the material 65G ( 65G, 65Г ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - 980 785 8 30 As-delivered state Band annealed to 1.5 650 15
Brinell hardness of the material 65G ( 65G, 65Г ) (annealing) , HB 10 -1 = 241 MPa Brinell hardness of the material 65G ( 65G, 65Г ) (without heat treatment) , HB 10 -1 = 285 MPa
Physical properties of the material 65G ( 65G, 65Г ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.15 37 7850 100 2.13 11.8 36 7830 490 200 2.07 12.6 35 7800 510 300 2 13.2 34 525 400 1.8 13.6 32 7730 560 500 1.7 14.1 31 575 600 1.54 14.6 30 590 700 1.36 14.5 29 625 800 1.28 11.8 28 705 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 65G ( 65G, 65Г ) . Weldability: is not used. Flakes : weakly predisposed Temper brittleness: predisposed
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены