Metals -> Corrosion-resistant (stainless) steel -> Corrosion-resistant steel for general purposes Characteristics of the material 10KH17N13M2T ( 10H17N13M2T, 10Х17Н13М2Т ).
Material : 10KH17N13M2T ( 10H17N13M2T, 10Х17Н13М2Т ) Classification : Corrosion-resistant steel for general purposes
Chemical composition in % of the material 10KH17N13M2T ( 10H17N13M2T, 10Х17Н13М2Т ) . C Si Mn Ni S P Cr Mo Cu - max 0.1 max 0.8 max 2 12 - 14 max 0.02 max 0.035 16 - 18 2 - 3 max 0.3 (5 С - 0.7) Ti, остальное Fe
Mechanical properties under Т=20o С of the material 10KH17N13M2T ( 10H17N13M2T, 10Х17Н13М2Т ) .
Assortment Dimension Direct. s в s T
d 5
y KCU Heat treatment - mm - MPa MPa % % kJ / m2 - Forging to 1000 510 196 35 45 Guenching 1050 - 1100o C, water, Sheet thin 530 38 Guenching 1050 - 1080o C,Cooling air, Bars 60 510 215 40 55 Guenching 1050 - 1100o C,Cooling air, Sheet trick 530 235 37 Guenching 1030 - 1080o C,Cooling air, Pipe cooling strain 529 35 Pipe hot strain 529 35
Brinell hardness of the material 10KH17N13M2T ( 10H17N13M2T, 10Х17Н13М2Т ) , Forging HB 10 -1 = 200 MPa
Physical properties of the material 10KH17N13M2T ( 10H17N13M2T, 10Х17Н13М2Т ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.06 7950 100 15.7 200 1.86 16.1 300 1.77 16.7 400 1.77 17.2 500 1.67 17.6 600 1.57 17.9 700 1.47 18.2 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 10KH17N13M2T ( 10H17N13M2T, 10Х17Н13М2Т ) . Weldability: without limitations.
Specification :
Mechanical properties : s в - Tensile strength , [MPa] s T - Yield stress, [MPa] d 5 - Specific elongation at fracture , [ % ] y - Reduction of area , [ % ] KCU - Impact strength , [ kJ / m2 ] HB - Brinell hardness , [MPa]
Physical properties : T - Test temperature , [Grade] E - Young modulus , [MPa] a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade] l - Termal (heat) condition coefficient , [Watt/(m·Grade)] r - Density , [kg/m3 ] C - Specific heat
( range 20o - T ), [J/(kg·Grade)] R - Electrical resistance , [Ohm·m]
Weldability : without limitations - welding is done without heating and subsequent heat treeting limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing