Metals -> High-temperature or heat-resistant steel and alloy -> Relaxation-resistant steel Characteristics of the material 25KH2M1F ( 25H2M1F, 25Õ2Ì1Ô ).
Material : 25KH2M1F ( 25H2M1F, 25Õ2Ì1Ô ) Classification : Relaxation-resistant steel
Chemical composition in % of the material 25KH2M1F ( 25H2M1F, 25Õ2Ì1Ô ) . C Si Mn Ni S P Cr Mo V Cu 0.22 - 0.29 0.17 - 0.37 0.4 - 0.7 max 0.25 max 0.025 max 0.03 2.1 - 2.6 0.9 - 1.1 0.3 - 0.5 max 0.2
Temperature of critical points of the grade 25KH2M1F ( 25H2M1F, 25Õ2Ì1Ô ).
Ac1 = 780 , Ac3 (Acm ) = 870 , Ar3 (Arcm ) = 790 , Ar1 = 700
Mechanical properties under Ò=20o Ñ of the material 25KH2M1F ( 25H2M1F, 25Õ2Ì1Ô ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Bar Æ 25 longitudinal 900 750 10 40 300 Normalizing 1030 - 1060o C,Drawing 680 - 720o C, air,
Brinell hardness of the material 25KH2M1F ( 25H2M1F, 25Õ2Ì1Ô ) (quenching, tempering) , HB 10 -1 = 235 - 277 MPa
Physical properties of the material 25KH2M1F ( 25H2M1F, 25Õ2Ì1Ô ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.23 7800 270 100 2.18 12.5 32.7 7780 536 360 200 2.13 12.9 31.8 7750 574 420 300 2.07 13.3 30.1 7720 599 500 400 2 13.7 28.5 7680 632 590 500 1.92 14 28.1 7650 674 710 600 1.83 14.7 26.4 7600 733 840 700 1.75 970 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 25KH2M1F ( 25H2M1F, 25Õ2Ì1Ô ) . Weldability: is not used.
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû