Characteristics of the material 10KH17N13M3T ( 10H17N13M3T, 10Х17Н13М3Т ).
Material :
10KH17N13M3T ( 10H17N13M3T, 10Х17Н13М3Т )
Classification :
Corrosion-resistant steel for general purposes
Chemical composition in % of the material 10KH17N13M3T ( 10H17N13M3T, 10Х17Н13М3Т ) .
C
Si
Mn
Ni
S
P
Cr
Mo
-
max 0.1
max 0.8
max 2
12 - 14
max 0.02
max 0.035
16 - 18
3 - 4
5(С - 0.7) Ti, остальное Fe
Mechanical properties under Т=20oС of the material 10KH17N13M3T ( 10H17N13M3T, 10Х17Н13М3Т ) .
Assortment
Dimension
Direct.
sв
sT
d5
y
KCU
Heat treatment
-
mm
-
MPa
MPa
%
%
kJ / m2
-
Bars
540
200
40
55
Guenching 1050 - 1100oC, air,
Sheet thin
530
38
Guenching Cooling water,
Sheet trick
530
235
37
Guenching 1030 - 1080oC,Cooling air,
Forging
510
196
35
40
Brinell hardness of the material 10KH17N13M3T ( 10H17N13M3T, 10Х17Н13М3Т ) , Forging
HB 10 -1= 200 MPa
Technological properties of the material 10KH17N13M3T ( 10H17N13M3T, 10Х17Н13М3Т ) .
Weldability:
without limitations.
Specification :
Mechanical properties :
sв
- Tensile strength , [MPa]
sT
- Yield stress, [MPa]
d5
- Specific elongation at fracture , [ % ]
y
- Reduction of area , [ % ]
KCU
- Impact strength , [ kJ / m2]
HB
- Brinell hardness , [MPa]
Weldability :
without limitations
- welding is done without heating and subsequent heat treeting
limited weldability
- welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability
- obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal trader