Metals -> Copper-zinc alloy (latten, brass) -> Copper-zinc alloys pressure treated Characteristics of the material LO70-1 ( LO70-1, ЛО70-1 ).
Material : LO70-1 ( LO70-1, ЛО70-1 ) Classification : Copper-zinc alloys pressure treated
Chemical composition in % of the material LO70-1 ( LO70-1, ЛО70-1 ) . Fe P Cu Pb Zn Sb Bi Sn Impurity max 0.07 max 0.01 69 - 71 max 0.07 27.2 - 30 max 0.005 max 0.002 1 - 1.5 all 0.3
Comment: Zn is a basis; the percentage of Zn is given approximately. Mechanical properties under Т=20o С of the material LO70-1 ( LO70-1, ЛО70-1 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - hard 680-750 3-5 soft 320-380 55-65
Brinell hardness of the material LO70-1 ( LO70-1, ЛО70-1 ) , hard HB 10 -1 = 145 - 155 MPa Brinell hardness of the material LO70-1 ( LO70-1, ЛО70-1 ) , soft HB 10 -1 = 55 - 65 MPa
Physical properties of the material LO70-1 ( LO70-1, ЛО70-1 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.05 117 8600 72 100 19.7
Friction coefficient of the material LO70-1 ( LO70-1, ЛО70-1 ) . Friction coefficient with oil
: 0.0082 Friction coefficient without oil
: 0.3
Technological properties of the material LO70-1 ( LO70-1, ЛО70-1 ) . Melting temperature, °C : 935 Forging temperature,°C : 650 - 750 Annealing temperature, °C : 550 - 650
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены