Metals -> Bronze -> Tin-free pressure-worked bronzes Characteristics of the material BrSr0.1 ( BrSr0.1, ÁðÑð0.1 ).
Material : BrSr0.1 ( BrSr0.1, ÁðÑð0.1 ) Classification : Tin-free pressure-worked bronzes
Chemical composition in % of the material BrSr0.1 ( BrSr0.1, ÁðÑð0.1 ) . Cu Ag Impurity 99.78 - 99.92 0.08 - 0.12 all 0.1
Comment: Cu is a basis; the percentage of Cu is given approximately. Mechanical properties under Ò=20o Ñ of the material BrSr0.1 ( BrSr0.1, ÁðÑð0.1 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - soft 200 80 55 hard 340 300 4
Brinell hardness of the material BrSr0.1 ( BrSr0.1, ÁðÑð0.1 ) , soft HB 10 -1 = 50 MPa Brinell hardness of the material BrSr0.1 ( BrSr0.1, ÁðÑð0.1 ) , hard HB 10 -1 = 110 MPa
Physical properties of the material BrSr0.1 ( BrSr0.1, ÁðÑð0.1 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.27 17 8890
Technological properties of the material BrSr0.1 ( BrSr0.1, ÁðÑð0.1 ) . Melting temperature, °C : 1082
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû