Metals -> Copper -> High-temperature cooper alloy Characteristics of the material BrNKHK ( BrNHK, ÁðÍÕÊ ).
Material : BrNKHK ( BrNHK, ÁðÍÕÊ ) Classification : High-temperature cooper alloy
Comment: Cu is a basis; the percentage of Cu is given approximately. Mechanical properties under Ò=20o Ñ of the material BrNKHK ( BrNHK, ÁðÍÕÊ ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - 800 780 10 50 1000
Brinell hardness of the material BrNKHK ( BrNHK, ÁðÍÕÊ ) , HB 10 -1 = 167 MPa Brinell hardness of the material BrNKHK ( BrNHK, ÁðÍÕÊ ) , deformed HB 10 -1 = 150 MPa Brinell hardness of the material BrNKHK ( BrNHK, ÁðÍÕÊ ) , annealed HB 10 -1 = 80 MPa
Physical properties of the material BrNKHK ( BrNHK, ÁðÍÕÊ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.4 196 8850 37.2
Technological properties of the material BrNKHK ( BrNHK, ÁðÍÕÊ ) . Forging temperature,°C : 750 - 950 Annealing temperature, °C : 750
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû