Metals -> Lead -> Lead

Characteristics of the material S3   ( 3 ).

Material : S3   ( 3 )
Classification : Lead


Chemical composition in % of the material S3   ( 3 ) .
Fe Cu As PbZn Ag Sb Bi Sn Impurity
max   0.005max   0.002max   0.005min   99.9max   0.005max   0.0015max   0.005max   0.06max   0.002 all 0.1


Mechanical properties under =20o of the material S3   ( 3 ) .
Assortment Dimension Direct. s sT d5 y KCU Heat treatment
- mm - MPa MPa % % kJ / m2 -
deformed     15   60-70   
casted     11-13  30-40   


    Brinell hardness of the material   S3   ( 3 )   ,     deformed HB 10 -1= 3 - 4.8   MPa
    Brinell hardness of the material   S3   ( 3 )   ,     casted HB 10 -1= 3.2 - 4.5   MPa


Physical properties of the material S3   ( 3 ) .
T E 10- 5 a 10 6 l r C R 10 9
Grade MPa 1/Grade Watt/(mGrade) kg/m3 J/(kgGrade) Ohmm
20 0.16 29.5   11340    



Specification :
Mechanical properties :
s - Tensile strength , [MPa]
sT - Yield stress, [MPa]
d5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2]
HB - Brinell hardness , [MPa]

Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion (range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(mGrade)]
r - Density , [kg/m3]
C - Specific heat ( range 20o - T ), [J/(kgGrade)]
R - Electrical resistance , [Ohmm]

Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others).
Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal trader