Metals -> Structural steel -> High quality structural carbon steel Characteristics of the material 15ps ( 15ps, 15ïñ ).
Material : 15ps ( 15ps, 15ïñ ) Substitute: 10êï, 20êï Classification : High quality structural carbon steel
Chemical composition in % of the material 15ps ( 15ps, 15ïñ ) . C Si Mn Ni S P Cr Cu As 0.12 - 0.19 0.05 - 0.17 0.35 - 0.65 max 0.25 max 0.04 max 0.035 max 0.25 max 0.25 max 0.08
Temperature of critical points of the grade 15ps ( 15ps, 15ïñ ).
Ac1 = 735 , Ac3 (Acm ) = 863 , Ar3 (Arcm ) = 840 , Ar1 = 685
Mechanical properties under Ò=20o Ñ of the material 15ps ( 15ps, 15ïñ ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Steel cold-drawn 392 8 50
Brinell hardness of the material 15ps ( 15ps, 15ïñ ) (annealing) , HB 10 -1 = 149 MPa Brinell hardness of the material 15ps ( 15ps, 15ïñ ) (cold-drawn, cold-worked) , HB 10 -1 = 187 MPa
Physical properties of the material 15ps ( 15ps, 15ïñ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.01 7850 100 1.92 12.4 53 7827 465 233 200 1.85 13.2 53 7794 486 296 300 1.72 13.9 49 7759 515 387 400 1.56 14.4 46 7724 532 487 500 14.8 43 7687 565 607 600 15.1 39 7648 586 753 700 15.3 36 7611 620 904 800 32 7599 691 1092 900 30 7584 708 1140 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 15ps ( 15ps, 15ïñ ) . Weldability: without limitations. Flakes : not predisposed Temper brittleness: not predisposed
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû