Metals -> Structural steel -> High quality structural carbon steel Characteristics of the material 20ps ( 20ps, 20ïñ ).
Material : 20ps ( 20ps, 20ïñ ) Substitute: 15êï Classification : High quality structural carbon steel
Chemical composition in % of the material 20ps ( 20ps, 20ïñ ) . C Si Mn Ni S P Cr Cu As 0.17 - 0.24 0.05 - 0.17 0.35 - 0.65 max 0.25 max 0.04 max 0.035 max 0.25 max 0.25 max 0.08
Temperature of critical points of the grade 20ps ( 20ps, 20ïñ ).
Ac1 = 735 , Ac3 (Acm ) = 850 , Ar3 (Arcm ) = 835 , Ar1 = 680
Mechanical properties under Ò=20o Ñ of the material 20ps ( 20ps, 20ïñ ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Steel cold-drawn 490 7 45
Brinell hardness of the material 20ps ( 20ps, 20ïñ ) (annealing) , HB 10 -1 = 163 MPa Brinell hardness of the material 20ps ( 20ps, 20ïñ ) (cold-drawn, cold-worked) , HB 10 -1 = 197 MPa
Physical properties of the material 20ps ( 20ps, 20ïñ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.12 100 2.08 12.3 51 7834 486 219 200 2.03 13.1 49 7803 498 292 300 1.97 13.8 44 7770 514 381 400 1.89 14.3 43 7736 533 487 500 1.77 14.8 39 7699 555 601 600 1.63 15.1 36 7659 584 758 700 1.4 15.2 32 7617 636 925 800 26 7624 703 1094 900 26 7600 703 1135 1000 695 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 20ps ( 20ps, 20ïñ ) . Weldability: without limitations. Flakes : not predisposed Temper brittleness: not predisposed
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû